Forming Acrylic Sheet Oven

Acrylic oven baking sheet aluminum foil timer felt for handling the acrylic and to prevent scratches tools for forming tools for forming may include.

Forming acrylic sheet oven.

This article uses a sheet about 1 4 thick so all times are about 10 to 15 minutes per step. We manufacture high qualitythermoforming equipment. For thicker sheets it will take longer and for thinner sheets it will take less time. It is important to provide sufficient clamping of the sheet during the forming process.

Solid surface ovens and vacuum formers pvc film and structural plastics formers and high pressure laminate formers postformers. A mold any object shape you can press the acrylic into to give it shape mallet and or a peen for shaping caution i ve only tried this in an electric oven. Plexiglass or acrylic sheet this system works well for small pieces of plexiglass in thicknesses of up to 1 8 inch. It is sheet temperature that dictates the process the end result being not just a better product but also decreased cycle time less scrap less floor space and reduced energy and labor costs.

So it happens that you have to use a separate mold on top and bottom platens. I can t recommend for. Generally the whole piece of plexiglas acrylic sheet is heated before forming in a hot air oven with forced circulation figure 1 the basic elementsof such an oven are an insulated chamber of suffi cient size which is provided with a means to force circulate the air and a means of heating which may be either gas or electricity. This refers to the process of vacuum and pressure forming of two sheets of polycarbonate simultaneously.

May not work for gas ovens. Twin sheet forming polycarbonate. Note that the minimum radius of the bend you create is 180 times the thickness of the plexiglass sheet. Force the plexiglass into the desired shape.

To reduce the length of the forming cycle pre dry the sheet in a spare oven and transfer it directly into the forming oven at 176 f 80 c after the drying period. The only major variable that can affect the forming process is the thickness of the plastic sheet. For instance the smallest complete circle you could form with a sheet of plexiglass 1 32 inch thick would have a radius of 5 6 inches. Sheet temperature is one of the most critical elements of the thermoforming process.

Attempting to create a smaller radius would snap the sheet. For thicker acrylic you will need to use a metal bar clamped very securely and you may only be able to work with narrow strips of material as your heat source may not be able to heat wider areas of thick material. After the plastic sheet is molded it stays in the molds then the two molds are brought together of course under high pressure.